Cold Repair
MRO 8011 - E PUTTY
| Brand | MRO Infra |
| Application | Bearing journals, Capacitors, Castings, Equipment, Gear box covers, Machinery, Pipelines, Pumps, Reactors, Sumps, Tanks, Transformers, Valves, Welded joints |
| Available Packaging | 500 g (A Part – 250 g & B Part 250 g Containers) |
| Packaging Type | Container |
| Shelf Life | 3 years from date of manufacture |
| Coverage | 1100cm²/kg @ 5mm |
| Mix Ratio | 1:1 (By Volume), 1:1 (By Weight) |
| Pot Life | 3 (At 30°C/ Mins) |
| Specific Gravity | 1.3 |
| Compressive Strength | 72 (Mpa) |
| Percent Solids (By Volume) | 100 |
| Specific Volume | 455 (CC/Kg) |
| Cured Shrinkage | 0.009 (Cm/Cm) |
| Temperature Resistance | Dry 93°C |
| Cured Hardness | 86 D (Shore D) |
| Dielectric Strength | 1.18 (KV/Mm) |
| Adhesive Tensile Shear | 14 (Mpa) |
| Thermal Expansion | 61 (Coefficient X10-6 CM/CM/°C) |
| Thickness | As Required (per Mm) |
| Recoat Time | 15-30 (Minutes) |
| Mixed Viscosity | Putty (Cps (Where Applicable)) |
MRO 8071 - E PUTTY
| Brand | MRO Infra |
| Application | Bearing journals, Capacitors, Castings, Equipment, Gear box covers, Machinery, Pipelines, Pumps, Reactors, Sumps, Tanks, Transformers, Valves, Welded joints |
| Available Packaging | 500 g (A Part – 250 g & B Part 250 g Containers) |
| Packaging Type | Container |
| Shelf Life | 3 years from date of manufacture |
| Coverage | 1100cm²/kg @ 5mm |
| Mix Ratio | 1:1 (By Volume), 1:1 (By Weight) |
| Pot Life | 3 (At 30°C/ Mins) |
| Specific Gravity | 1.3 |
| Compressive Strength | 72 (Mpa) |
| Percent Solids (By Volume) | 100 |
| Specific Volume | 455 (CC/Kg) |
| Cured Shrinkage | 0.009 (Cm/Cm) |
| Temperature Resistance | Dry 93°C |
| Cured Hardness | 86 D (Shore D) |
| Dielectric Strength | 1.18 (KV/Mm) |
| Adhesive Tensile Shear | 14 (Mpa) |
| Thermal Expansion | 61 (Coefficient X10-6 CM/CM/°C) |
| Thickness | As Required (per Mm) |
| Recoat Time | 15-30 (Minutes) |
| Mixed Viscosity | Putty (Cps (Where Applicable)) |
MRO 8003 - FLEX PUTTY
| Available Packaging | 500 Gm (A Part: 333 gm & B Part: 167 gm) Containers |
| Packaging Type | Container |
| Shelf Life | 3 years from date of manufacture |
| Coverage | 1016 Cm2 / 0.5kg / 2.5 mm (cm2/pack size/thickness) |
| Mix Ratio | 2:1 (By Volume – Manual), 2:1 (By Weight – Manual) |
| Pot Life | 10 Mins (@ 30°C – IS 101) |
| Specific Gravity | 1.05 (ASTM D 1475-98) |
| Compressive Strength | 21 (ASTMD 695 N/mm2) |
| Appearance | Thick Paste |
| Max. Operating Temp. | 82°C (Dry) |
| Adhesive Shear Strength | 16 (ASTM D1002 N/mm2) |
| Maximum Elongation | 600 (percent) |
| Hardness Shore | 86 (A ASTM D 2240) |
MRO 8024 - PIPE WRAP (100mm X 9m)
| Brand | MRO Infra |
| Application | Corroded pipes, Force mains, Gravity lines, Irregular pipe fittings, Joints, Pipes & fittings, Tees |
| Available Packaging | 1 No (100mm x 9 m) Hermetically sealed foil pouch |
| Packaging Type | Hermetically sealed foil pouch |
| Shelf Life | 2 years from date of manufacture |
| Compressive Strength | 7380 psi (518.86 kg/cm2 ) |
| Temperature | 135°C (Dry), 240°C (Intermittent), 71°C (Wet) |
| Tensile Strength | 6000 psi (421.84 kg/cm2 ) |
| Flexural Strength | 4550 psi (319.89 kg/cm2 ) |
| Lap Shear Strength | >2000 psi (137.89 bar) (140.61 kg/cm2 ) |
| Hardness | 34 Shore D |
| Max Pressure | 2700 psi (189.82 kg/cm2 ) |
| Flexibility | 3.2% elongation at break |
| Active gravity flow leak | 15 psi (1.05 kg/cm2 ) or less |
| Abrasion Resistance | 34 mg/1000 cycles (Taber Abrasion-CS17/1000 gm) |
MRO 8022 - PIPE WRAP (50mm X 3.6m)
| Brand | MRO Infra |
| Application | Corroded pipes, Force mains, Gravity lines, Irregular pipe fittings, Joints, Pipes & fittings, Tees |
| Available Packaging | 1 No (100mm x 9 m) Hermetically sealed foil pouch |
| Packaging Type | Hermetically sealed foil pouch |
| Shelf Life | 2 years from date of manufacture |
| Compressive Strength | 7380 psi (518.86 kg/cm2 ) |
| Temperature | 135°C (Dry), 240°C (Intermittent), 71°C (Wet) |
| Tensile Strength | 6000 psi (421.84 kg/cm2 ) |
| Flexural Strength | 4550 psi (319.89 kg/cm2 ) |
| Lap Shear Strength | >2000 psi (137.89 bar) (140.61 kg/cm2 ) |
| Hardness | 34 Shore D |
| Max Pressure | 2700 psi (189.82 kg/cm2 ) |
| Flexibility | 3.2% elongation at break |
| Active gravity flow leak | 15 psi (1.05 kg/cm2 ) or less |
| Abrasion Resistance | 34 mg/1000 cycles (Taber Abrasion-CS17/1000 gm) |
MRO 8001 - S PUTTY
| Brand | MRO Infra |
| Application | Bearing housings, Engine casings, Flanges, Hydraulic rams, Load bearing shims, Pipes, Pitted metal surfaces, Pump casings, Shafts, Tanks |
| Industries | Mechanical |
| Available Packaging | 1 Kg ( A Part – 0.8 Kg & B Part 0.2 Kg Containers) |
| Packaging Type | Container |
| Shelf Life | 3 years from date of manufacture |
| Coverage | 770cm2/kg @ 5mm |
| Dielectric Strength | 2.2 (Kv/Mm) |
| Mix Ratio | 4:1 (By Weight), 4.5:1 (By Volume) |
| Percent Solids (By Volume) | 100 |
| Pot Life | 20-25 (At 30°C/ Mins) |
| Specific Volume | 424 (Cc/Kg) |
| Cured Shrinkage | 0.001 (Cm/Cm) |
| Cured Hardness | 87 D (per Shore D) |
| Specific Gravity | 2.0-2.5 |
| Temperature Resistance | Dry 177°C Wet 65°C |
| Adhesive Tensile Shear | 14 (N/mm2) |
| Compressive Strength | 120 (N/mm2) |
| Thermal Expansion | 40 (Coefficient X10-6 Cm/Cm/°C) |
| Thickness | As Required (per Mm) |
| Recoat Time | 4 (per Minutes) |
| Mixed Viscosity | Putty (per Cps (Where Applicable)) |
| Functional Cure | 24 hrs |
MRO 8051 - S STICK
| Brand | MRO Infra |
| Application | Boats, Boilers, Butterfly valves, Concrete sewer pipes, Condensers, Cooling pump impellers, Cracks, Heat exchanger coils, Heat exchangers, Hulls of ships, Industrial vessels, Leakages, Metal fabrications, Storage tanks, Threads, Trawlers, Water supply mains |
| Available Packaging | 114 gm (4 oz) Co-centric Stick |
| Packaging Type | Co-centric Stick |
| Shelf Life | 2 years from date of manufacture |
| Compressive Strength | 850 Kg/Sq Cm |
| Temperature Resistance | 125°C (Working Temperature), 150°C (Intermittent Temperature) |
| Tensile Strength | 75 Kg/Sq cm (Shear) |
| Flexural Strength | 500 Kg/Sq Cm |
| Appearance | Grey |
| Mix Ratio | 1:1 (By Volume) |
| Complete Cure | 2 hrs |
| Cured Hardness | 80 (per Shore D) |
| Dielectric Strength | 300 (volts/mil) |
| Working Life | 3 Minutes |
| Cure | Room Temperature |
| Chemical Resistance | Hydrocarbons, ketones, alcohols, esters, halocarbons, aqueous salt solutions and dilute acids and bases. |
| Shrinkage (%) | <1 |
| Non Volatile content | 100 |
MRO 8000 - Ti PUTTY
| Brand | MRO Infra |
| Application | Boats, Boilers, Butterfly valves, Concrete sewer pipes, Condensers, Cooling pump impellers, Cracks, Heat exchanger coils, Heat exchangers, Hulls of ships, Industrial vessels, Leakages, Metal fabrications, Storage tanks, Threads, Trawlers, Water supply mains |
| Industries | Mechanical |
| Available Packaging | 1 Kg ( A Part – 0.8 Kg & B Part 0.2 Kg Containers) |
| Packaging Type | Container |
| Shelf Life | 3 years from date of manufacture |
| Coverage | 848cm2/kg @ 5mm |
| Dielectric Strength | 2.2 (Kv/Mm) |
| Mix Ratio | 4:1 (By Weight), 7:1 (By Volume) |
| Percent Solids (By Volume) | 100 |
| Pot Life | 25 (At 30°c/ Mins) |
| Specific Volume | 424 (Cc/Kg) |
| Cured Shrinkage | 0.001 (Cm/Cm) |
| Cured Hardness | 87 D (per Shore D) |
| Specific Gravity | 2.36 |
| Temperature Resistance | Dry 177°C Wet 65°C |
| Adhesive Tensile Shear | 14 (per Mpa) |
| Compressive Strength | 105 (Mpa) |
| Thermal Expansion | 40 (Coefficient X10-6 Cm/Cm/°C) |
| Thickness | As Required (per Mm) |
| Recoat Time | 4 (per Minutes) |
| Mixed Viscosity | Putty (per Cps (Where Applicable)) |
MRO 8012 - UW PUTTY
| Brand | MRO Infra |
| Application | Equipment, Offshore drilling, Paper mills, Pipes & fittings, Potable water leakages, Pulp mills, Pumps, Tanks, Valves, Water treatment plants, Welded joints |
| Available Packaging | 1 Kg (A Part 643 gm & B Part 357 gm Containers) |
| Packaging Type | Container |
| Shelf Life | 3 years from date of manufacture |
| Coverage | 1100cm²/kg @ 5mm |
| Mix Ratio | 3 (At 30°C/ Mins) |
| Pot Life | 3 (At 30°C/ Mins) |
| Specific Gravity | 1.3 |
| Compressive Strength | 65 (N/mm2) |
| Percent Solids (By Volume) | 100 |
| Specific Volume | 455 (CC/Kg) |
| Cured Shrinkage | 0.009 (Cm/Cm) |
| Temperature Resistance | Dry 93°C |
| Cured Hardness | 85 D (Shore D) |
| Dielectric Strength | 1.06 (KV/Mm) |
| Adhesive Tensile Shear | 19 (N/mm2) |
| Thickness | 1.6 minimum (Per Coat / mm) |
| Mixed Viscosity | Putty (Cps (Where Applicable)) |
| Thermal Expansion | 61 (Coefficient X10-6 CM/CM/°C) |