SEALANTS
GP: General Purpose
| Curing System | Moisture Cure |
| Skin formation (20°C / 65% R.H.) | Ca 7 min. |
| Curing Rate (20°C / 65% R.H.) | Ca 2 mm/24h |
| Hardness (DIN 53505) | 17 ± 5 Shore A |
| Specific Gravity (DIN 53479) | Ca 0.95 g/ml |
| Temperature Resistance | -60°C to +120°C |
| Elastical Recovery (ISO 7389) | >80% |
| Maximum allowed Distortion | 20% |
| Elasticity Modulus 100% (DIN 53504) | 0.25 N/mm² |
| Maximum Tension (DIN 53504) | 1.25 N/mm² |
| Elongation at Break (DIN 53504) | > 800% |
| Color: | Packaging: | |
| White, Black, Transparent, Grey | 260ml |
GP Plus: General Purpose Plus
| Curing System | Moisture Cure |
| Skin formation (20°C / 65% R.H.) | Ca 7 min. |
| Curing Rate (20°C / 65% R.H.) | Ca 2 mm/24h |
| Hardness (DIN 53505) | 20 ± 5 Shore A |
| Specific Gravity (DIN 53479) | Ca 1.00 g/ml |
| Temperature Resistance | -60°C to +150°C |
| Elastical Recovery (ISO 7389) | > 90% |
| Maximum allowed Distortion | 25% |
| Elasticity Modulus 100% (DIN 53504) | 0.30 N/mm² |
| Maximum Tension (DIN 53504) | 1.40 N/mm² |
| Elongation at Break (DIN 53504) | > 800% |
| Color: | Packaging: | Product Shade Card: |
| White, Black, Transparent, Grey | 280ml |
AP: All Purpose
Trade Grade Neutral Silicone Sealant Description:
AP is a high performance silicone sealant with outstanding sealing properties to porous & non – porous substrates.
Applications :
Buildingandconstructionjoints.Topsealingatglazingjobs.Sealingbetweentreatedwoodandglass.Sealing betweenPVCandglass.Automotive/BusGlass sealing, uPVC profiles, concrete, brick masonry, ACP, Aluminium&hardware applications.
Properties :
| Curing System | MoistureCure |
| Skin formation (20°C / 65% R.H .) | Ca 10 min. |
| Curing Rate (20°C / 65%R.H.) Hardness(DIN 53505) | Ca 1 to 2 mm/24h |
| Specific Gravity (DIN534 79) | 25±5 Shore A |
| TemperatureResistance | Ca 1.18 g/ml |
| Elastical Recovery(DIN 7389) | -60°Cto+120°c |
| MaximumallowedDistortion | >80% |
| ElasticityModulus 100% (DIN 53504) | 25.00% |
| MaximumTension (DIN 53504) | 0.38N/mm2 |
| Elongationat Break (DIN 53504) | 1.00N/mm2 |
Characteristics :
Stays elastic aftercuring
Non-sag,Pasteconsistency
Excellent adhesion to most common industrial and buildingmaterials
Solutiontoeliminate leakages in windscreens,tail lights and fixed glasspanels
Maintains a flexible seal and safe to use on most of the commonpaints
IS : Industrial Seal
Industrial Grade Neutral Silicone Sealant
Description :
IS is a high performance neutral cure silicone sealant with outstanding adhesive/sealing properties for most of the critical industrial applications.
Applications :
ISis the most suitable industrial grade silicone sealant. Sealing of lock seams, joints in ductwork,welds and fasteners in metal fabrication, dissimilar metalsand corrosion sensitive surfaceslikechromeandsteel.Building and construction joint s.Sealing between treated woodand glass.Sealing betweenPVCandglass.
| Curing System | Moisture Cure |
| Skin formation (20°C / 65% R.H .) | Ca 10 min. |
| Curing Rate (20°C / 65%R.H.) Hardness(DIN 53505) | Ca 1 to 2 mm/24h |
| (20°C/65%R.H.)Hardness(DIN 53505) | 25±5 Shore A |
| Specific Gravity (DIN534 79) | Ca 1.18 g/ml |
| Temperature Resistance | -60°C to+120°c |
| Elastical Recovery(DIN 7389) | > 80% |
| Maximum allowed Distortion | 25.00% |
| Elasticity Modulus 100% (DIN 53504) | 0.38N |
| Maximum Tension (DIN 53504) | 1 mm2 |
| Elongationat Break (DIN 53504) | 600% |
Characteristics
One component RTV (RoomTemperatureVulcanizes)
Excellent UVresistance
Can be applied to overhead or verticaljoints
Does not crack, crumble or dry out in directsunlight
·Bondsalmostallsurfaces:metals,paintedsurfaces,glasses, ceramics,mostplastics, non-oily woods, fibrous cement and concretesurfaces
Color
White, Black,Transparent, Grey
Packaging
280ml
MB : Multi Bond
High Performance Multi-Application Adhesive Description
Multi Bond is ideal for bonding timber, most of the common construction materials and mirror s. It is asyntheticrubber based adhesive especially designed for mirror bonding and ACPbonding application inbuildings.
Applications
MultiBond is very suitableforbonding of mirror, skirting boards, cornices, concrete, brick, alu minium,metals, wood, tiles, ceramics, varnished or painted surfaces and many plasticsetc.
| Base | Synthetic Rubber (SBR) |
| Consistency | Paste |
| Curing System | Physical drying and crystallization |
| Specific Gravity (DIN 534 79) | 1.23 g/ml |
| Open Time* | 15 min. |
| Curing Time* | 20 min.(initial strength), 24-48 h |
| Temperature Resistance | -20°C to +60°C (cured) |
Color
Beige
Packaging
390 g
Silirub MP
Professional Grade Acetoxy Silicone Sealant Description
SilirubMPisaonepartaceticcuresiliconesealant.Astrong,fastcuring,multi-purposesealant,itisunaffectedby rain, sunlight, snow etc.It is formulated with McCoy Soudal’s years of experience on a widerangeof applications. Silirub MP has ahighUV and waterresistance.
Applications
SilirubMPis very much suitable for Automobiles,Buses,Construction work, Glass,House(DIY), Aluminiu m,Refrigeration,ACductsealing, non oily wood etc.
| Curing System | Moisture Cure |
| Skin formation (20°C / 65% R.H .) | Ca 7 min. |
| Curing Rate (20°C / 65%R.H.) | Ca 2 rmn/24h |
| Hardness(DIN 53505) | 20±5 Shore A |
| Specific Gravity (DIN534 79) | Ca 1.00 g/ml |
| Temperature Resistance | -60°C to+150°C |
| ElasticalRecovery(ISO 7389) | >90% |
| Maximum allowed Distortion | 25.00% |
| Elasticity Modulus 100% (DIN 53504) | 0.30N/mm2 |
| Maximum Tension (DIN 53504) | 1.40 N/mm2 |
| Elongationat Break (DIN 53504) | > 800% |
Characteristics
• Excellentbonding on most of thesurfaces
• Colorstability
• Good UV resistance
• Easytooling and soft extrude ableproperties
• RTV-Room TemperatureVulcanization
• Non-sag
• Longshelflife
Colour
White, Black, Transparent, Grey
Packaging
280ml
Silirub GS
Glass Seal 100% Acetoxy Silicone Sealant
Description
Silirub GS is one component, elastic high quality100%acetoxy silicone sealant.
Applications
Sealing of glasses, air-conditioning ducts, spider glazing, connection joints inGlass Facades,Aquarium, top sealingfor Glass toGlassat glazing job s.
| Curing System | Moisture Cure |
| Skin formation (20°C / 65% R.H .) | Ca 7 min. |
| Curing Rate (20°C / 65%R.H.) | Ca 2 mm/24h |
| Hardness(DIN 53505) | 25±5 Shore A |
| Specific Gravity (DIN534 79) | Ca 1.03 g/ml |
| Temperature Resistance | -60°C to+180°C |
| ElasticalRecovery(ISO 7389) | >90% |
| Maximum allowed Distortion | 25.00% |
| Elasticity Modulus 100% (DIN 53504) | 0.40N/mm2 |
| Maximum Tension (DIN 53504) | 1.50N/mm2 |
| Elongationat Break (DIN 53504) | >800% |
Characteristics
▪ Specially designed for spider glazing applications in buildingindustries.
▪ Performbetter even if used for sealing inbutt joints of glass
▪ Excellent bonding on most of the common construction/buildingsubstrates
▪ One part – moisturecure
▪ Excellent UVresistance
▪ Fastcure
Color
Transparent, Black
Packaging
300ml
Silirub CS
Superior Grade Construction Silicone Sealant Description
Silirub CS is a high-quality neutral curelowmodulus silicone sealant with high elasticity which is based on alkox y technolog y.
Applications
All the usual building and construction joints
All glazing jobs
Expansion joints between different building materials
Perfectly suitable on polycarbonate joints
| Curing System | Moisture Cure |
| Skin formation (20°C / 65% R.H .) | Ca 10-15 min. |
| Curing Rate (20°CI65%RH) | Ca1.5mm/24h |
| Hardness (DIN 53505) | 20±5 ShoreA |
| Specific Gravity (DIN534 79) | 1.03 g/ml |
| Temperature Resistance | -40°C to+120°c |
| Elastical Recovery (ISO 7389) | >80% |
| Maximum allowed Distortion | 25.00% |
| Elasticity Modulus 100% (DIN 53504) | 0.35N/mm2 |
| Maximum Tension (DIN 53504) | 1.60 N/mm2 |
| Elongationat Break (DIN 53504) | >600% |
Characteristics
▪ Very easytoapply
▪ Permanentlycolorfast
▪ UV-resistant
▪ Stays fully elastic aftercuring
▪ Very good adhesion on most types ofmaterials
▪ Almost nosmell
▪ ShinyColors
▪ Hightransparency in clearversion
Color
BrilliantWhite,Transparent, Black,Grey
Packaging
300ml
Silirub Cleanroom
FDA Approved Neutral Silicone Sealant
Description
Silirub Cleanroom is a high-quality neutral, elastic silicone sealant. The product has been developed for seahny, applications in critical surroundings (hospitals, laboratories, pharmaceutical industry) and in food safe applications.
Applications
Sealing in cleanroom applications and sealing in environments where food is handled and stored (food container: cold store installations, food industry, etc.)
| Curing System | Moisture Cure |
| Skin formation (20°C / 65% R.H .) | Ca 30 min. |
| Curing Rate (20°CI65%RH) | Ca1.5 mm/24h |
| Hardness (DIN 53505) | 20±5 ShoreA |
| Specific Gravity (DIN534 79) | 1.36 g/ml |
| Temperature Resistance | -50°C to+120°c |
| Elastical Recovery (ISO 7389) | >80% |
| Maximum allowed Distortion | 25.00% |
| Elasticity Modulus 100% (DIN 53504) | 0.35N/mm2 |
| Maximum Tension (DIN 53504) | 2 N/mm2 |
| Elongationat Break (DIN 53504) | > 1200% |
Characteristics
• Permanent color. UV-resistant
• Stays very elastic after curing
• Very good adhesion on many materials
• Almost no smell
• Sow skinning time therefore dally suited for long joint runs
• Tested according to FDA regulations code CFT 21 $ 177.2600 (e) and (f)
Color
White, other colours on request
Packaging
300 ml
Soudaseal 250XF
High Performance Fast Cure Sealant Adhesive
Description
Soudaseal 250XF is high quality, neutral, one component adhesive/sealant with a high initial tack based on MS-Polymer technology.
Applications
Structural bonding applications in automobile industries (Cars, buses, trucks, marine, trains etc.) solar panel and wind mill applications. Structural elastic bonding in building and metal working industries. Elastic bonding of panels, profiles and other pieces on most of the common substrates.
| Curing System | Moisture Cure |
| Skin formation (20°C / 65% R.H .) | Ca 5 min. |
| Curing Rate (20°CI65%RH) | 3 mm/24h |
| Hardness (DIN 53505) | 50+5 shore A |
| Elastical Recovery (ISO 7389) | 1.47 g/ml |
| Specific Gravity (DIN534 79) | >75% |
| Temperature Resistance | 20.00% |
| Temperature Resistance | -40C to +90C |
| elastity modulus 100% (DN 53504 ) | 1.60 N/ mm2 |
| Tear Strength ( DN 53504 ) | 3.00 N/ mm2 |
| Elongationat Break (DIN 53504) | 500.00% |
| Shear Strength | > 2 N/mm2 |
| Substrate | A|MgSi1 |
| Thickness | 2mm |
| Shear Velocity | 10mm/min |
Adhesion
Soudaseal 250XF has an excellent adhesion on almost all substrates. McCoy MS 50 has been experimented on the following metal surfaces: polycarbonate (Makrolon, polyamida. steel, AlMgSll . brass. PVC, electrolytic galvanized steel, PMMA, AJCuMg1, fame galvanized steel, AlMg1 and steel ST1403, polystyrene, ABS, pass fiber reinforced epoxy and polyester (GRP). Use of Surface Activator for optimum adhesion is always advisable.
Characteristics
• High performance mechanical properties
• Combines hipi stiffness with very high tend strength
• High green strength, quick build-up of end strength, hipi sheer strength after full cure
• Does not contain isocyanates, silicone, solvent
• Flexible elastic rubber – movement accommodation up to 20%
• No bubble formation within sealant (in high temperature and humidiry applicalths)
• Color stability and LW resistance
• Can be painted wet-on-wet in paint trains with most industrial paints
• Withstands all climatic conditions
• Minimal health and safety considerations
Colour
White. Black. Grey. Beige
Packaging
293 ml cartridges and 600 ml sausages
Soudaseal 240FC
High Performance General Purpose Sealant Adhesive
Description
Soudaseal 240FC is high quality single component joint sealant with high adhesive strength. It is based on MS-Polymerl chemically neutral and fully elastic.
Applications
Bonding and sealing in building industry. Sealing of floor joints, low movement wall joints, connection joints in sheet metal fabrication, structural bonding in vibrating constructions, sealing of air-conditioning systems. Also used in sanitary applications, safety and security glass bonding applications and supple bonding in caravans, containers, car bodies, solar panels, wind mill application and automobile applications, etc.
| Curing System | Moisture Cure |
| Skin formation (20°C / 65% R.H .) | Ca 5 min. |
| Curing Rate (20°CI65%RH) | 2-3 mm/24h |
| Hardness (DIN 53505) | 40+5 shore A |
| Elastical Recovery (ISO 7389) | >75% |
| Specific Gravity (DIN534 79) | 1.67 g/ml |
| Maximum Deformation | 20.00% |
| Temperature Resistance | -40C to +90C |
| elastity modulus 100% (DN 53504 ) | 0.75 N/ mm2 |
| Tear Strength ( DN 53504 ) | 1.80 N/ mm2 |
| Elongationat Break (DIN 53504) | 750.00% |
| Shear Strength | 0.9 N/mm2 |
| Substrate | A|MgSi1 |
| Thickness | 2mm |
| Shear Velocity | 10mm/min |
Adhesion
Soudaseal 240FC has an excellent adhesion on almost all substrates. Soudaseal 240FC has been experienced on the following metal surfaces: polycarbonate (Makrolon°), polyamide. steel. AlMg3i1, brass. PVC. electrolytic galvanized steel, PMMA, AlCuMgi , flame galvanized steel, AlMg and steel ST1403, polystyrene. ABS. glass fiber reinforced epoxy and polyester (GRP). While producing plastics very often releasing agents, processing aids and other protective agents are used. Use of Surface Activator for optimum adhesion is always advisable.
Characteristics
• Outstanding bond strength on nearly all surfaces, even on slightly wet surfaces
• Flexibleelastic rubber
• Straightforward application even in adverse conditions
• No bubble formation within sealant (in high temperature and humidityappications)
• Very easy to tool and finish
• Good exttudeabikty even at low temperatures
• Good color stability, weather and LW resistance
• Ecological advantages – free of isocyanates, solvents. halogens and acids
• Minimal health and safety considerations
• Can be painted with all water based paints and manyother systems
• No staining of porous materials such as natural stone, granite. marble. etc
Colour
White, Black. Grey. Beige, Concrete Grey
Packaging
290 ml cartridges and 600 ml sausages
Gasketseal
| Packaging: | Product Shade Card: | |
| 32g |
Fire Silicone B1 FR
| Base | Polysiloxane |
| Consistency | Stable Pasta |
| Curing System | Moisture Cure |
| Skin Forming | Ca 20 min. (20°C/65% R.H.) |
| Curing Time* | 1mm/24h |
| Shore A Hardness | 16 Shore A |
| Specific Gravity | Ca 1,17g/cm³ |
| Temperature Resistance | -40°C until +140°C |
| Elongation at Break | 900% (DIN52455) |
| E-Modulus 100% | 0,20N/mm² (DIN52455) |
| Elastical Recovery | >90% (DIN52455) |
| Maximum Deformation | ±25% |
| Color: | Packaging: | Product Shade Card: |
| White, Grey | 310ml, Foilbag 600ml | |
| Click here to download: TDS | Sealants Usage Calculator | ||
Firecryl FR
| Base | Acrylic Dispersion |
| Consistency | Pasta |
| Curing System | Physical drying |
| Skin formation (20°C/65% R.H.) | Approx. 20 min. |
| Shrinkage (DIN 52451) | Approx. 15% |
| Specific Gravity (DIN 53479B) | 1,40 g/ml |
| Temperature Resistance | -20°C to +80°C |
| Maximum allowed Distortion | 10% |
| Color: | Packaging: | Product Shade Card: |
| White, Grey | 310ml, Foilbag 600ml | |
| Click here to download: TDS | Sealants Usage Calculator | ||
Soudaflex Construction FC
| Base | Polyurethane |
| Consistency | Paste |
| Curing System | Moisture Cure |
| Skin formation (20°C/65% R.H.) | Ca 15 min. |
| Curing Rate (20°C / 65% R.H.) | Ca 3 mm/24h |
| Hardness (DIN 53505) | 40 ± 5 Shore A |
| Specific Gravity (DIN 53479) | 1,30 g/ml |
| Temperature Resistance | -30°C to +90°C |
| Elastic Recovery (DIN 7389) | > 80% |
| Maximum allowed Distortion | 20% |
| Elasticity Modulus 100% (DIN 53504) | 0.80 N/mm² |
| Maximum Tension (DIN 53504) | 1.70 N/mm² |
| Elongation at Break (DIN 53504) | 700% |
| Color: | Packaging: | Product Shade Card: |
| White, Grey, Black, Other colours on request | Cartridge 310ml, Sausage | |
| 300ml, 400ml, 600ml | ||
| Click here to download: TDS | Sealants Usage Calculator | ||
polyurethane sealant for wide range of sealing and bonding applications.
applications in the building industry.
constructions.
applications.